Synthesis and Characterization of Thermally-Reduced Graphene
|
|
|
|
|
|
|
|
نویسنده
|
Jabari seresht Razieh ,Jahanshahi Mohsen ,Rashidi Ali Morad ,Ghoreyshi Ali Asghar
|
|
منبع
|
iranica journal of energy and environment - 2013 - دوره : 4 - شماره : 1 - صفحه:53 -59
|
|
چکیده
|
Thermally-reduced graphene was obtained from reduction of graphene oxide (go) via heat treatment under the hydrogen in the range of 300-1100°c. in order to find optimum tempreture, the synthesized graphene has been investigated by x-ray diffraction (xrd), ftir spectroscopy as well as raman spectroscopy. the result indicated that the reduced graphene at 900°c (gr900) had the highest quality in comparison with the other temperatures. additionally, gr900 exhibited a sharp (002) peak corresponding to an interlayer distance of 3.39° a, which is close to that of conventional graphene (3.4°a). however, the structure of gr900 was also investigated by transmission electron microscopy (tem), scanning electron microscopy (sem) and the results supported the previous findings
|
|
کلیدواژه
|
Graphene ,Graphene oxide ,Thermal reduction ,X-ray diffraction ,FTIR spectroscopy ,Raman spectroscopy
|
|
آدرس
|
babol noshirvani university of technology, Nanotechnology Research Institute, Faculty of Chemical Engineering, ایران, babol noshirvani university of technology, Nanotechnology Research Institute, Faculty of Chemical Engineering, ایران, Research Institute of Petroleum Industry, Nanotechnology Research Center, ایران, babol noshirvani university of technology, Nanotechnology Research Institute, Faculty of Chemical Engineering, ایران
|
|
پست الکترونیکی
|
mjahan@nit.ac.ir / mmohse@yahoo.com
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|