Magneto-Optical Properties of Gap Single Crystal
|
|
|
|
|
نویسنده
|
Omar M S ,Abbas T A
|
منبع
|
پژوهش فيزيك ايران - 1388 - دوره : 9 - شماره : 4 - صفحه:98 -102
|
|
|
چکیده
|
The temperature dependence of magneto-optical and magneto-photoconductivity measurements were carried out in the range of(200-330) k. a home made optical cryostat was used for the measurements. the measured room temperature value of the energy gapwas found to be 2.211 ev. the temperature coefficient of energy gap was found to be -5.48 x 10-4 ev/k obtained by the opticalabsorption method and -4.90 x 10-4 ev/k from the measurements of photoconductivity. the magnetic field coefficien: of energy gapwas found to be temperature dependent with values of 1.34 x 10-3 ev/tesla at 202 k and 2.67 x 10-3 ev/tesla at roo n temperature,when the field used was up to 2.2 tesla. the reduced effective mass of carriers are also calculated from both techniques and found tobe changing from 0.034 rno to 0.021 rno when magneto-optical data was used in the calculations and from 0.052 rno to 0.032 rno whenmagneto-photoconductivity data was used as the temperature changed from 220 k to 330 k respectively.
|
کلیدواژه
|
Magneto-Optical Properties ,Photoconductivity ,Semiconductors ,Gap
|
آدرس
|
University Of Salahaddin, College Of Science, Deparment Of Physics, Iraq, University Of Salahaddin, College Of Science, Department Of Physics, Iraq
|
پست الکترونیکی
|
dr_m_s_omar@yahoo.com
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|