The Effect of Two Shading Techniques on Value of Zirconia-Based Crowns
|
|
|
|
|
نویسنده
|
Ahangari Ahmad Hassan ,Torabi Ardakani Kianoosh ,Mahdavi Farideh ,Torabi Ardakani Mahshid
|
منبع
|
Journal Of Dentistry, Shiraz University Of Medical Sciences - 2015 - دوره : 16 - شماره : 2 - صفحه:129 -133
|
|
|
چکیده
|
Statement of the problem: by introducing the coloring liquids, it is claimed that it is possible to make the color of frameworks fabricated from zirconium oxide extremely close to the natural tooth color.purpose: the purpose of this research was to evaluate the effect of two staining techniques on value changing in zirconia crowns.materials and method: three groups a, b, and c, each containing ten zirconia crowns, were used. the zirconium cores samples were fabricated by a cad/cam device. group a was left uncolored, groups b was submerged for two minutes in a2 coloring liquid and group c was stained with brush. then all cores were sintered and the porcelain was applied by using the layering technique. ultimately, the crowns color was determined using a spectrophotometer. their color changing (?e) and value changing (?l) in relation to a2 color were also assessed. the data were analyzed with one-sample t-test, posthoc tukey, and one-way anova tests with significant level set at 0.05.results: the mean value in all groups was higher than the value obtained from a2 color samples (p= 0.001). the highest mean value was 78.31±1.22 belonging to group c (staining with brush) and the lowest mean value was 76.99±0.65 belonging to group b (submerging). the results of post-hoc tukey regarding both ?e and ?l variables showed a significant difference between groups a (uncolored) and c (staining with brush) with p?e=0.006 and p?l=0.039, respectively. a significant difference between group b (submerging technique) and c (staining with brush) were shown when these two variables were compared (p?e=0.001, p?l=0.015).conclusion: due to the higher value increase in surface staining (brush), it is recommended to use the submerging technique for staining zirconia cores.
|
کلیدواژه
|
Zirconia ,Color ,Crown ,Value ,Spectrophotometer
|
آدرس
|
Shiraz University Of Medical Sciences, ایران, Shiraz University Of Medical Sciences, ایران, Shiraz University Of Medical Sciences, ایران, Private Dentist, Shiraz, Iran., ایران
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Authors
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|